Hybrid composite journal bearing and manufacturing method thereof

ABSTRACT

The object of this invention is to provide a hybrid composite journal bearing which is constructed so that a composite liner is positioned on an inner surface of a metal housing having a circular cross-section, thus preventing a journal from being damaged or seized to the bearing, due to friction between the metal or composite journal and the journal bearing. The hybrid composite journal bearing ( 210 ) includes a metal housing ( 211 ) which is secured on an outer surface thereof to a bearing system and has a circular cross-section A composite liner ( 212 ) is laminated to an inner surface of the metal housing ( 211 ) with a uniform thickness so as to minimize friction between the journal bearing and a journal.

TECHNICAL FIELD

The present invention relates, in general, to journal bearings and, moreparticularly, to a hybrid composite journal bearing constructed so thata composite liner is positioned on an inner surface of a metal housinghaving a circular cross-section. In particular, the present inventionrelates to a method of manufacturing such a hybrid composite journalbearing.

BACKGROUND ART

FIG. 1 is a schematic view to show a bearing system equipped withjournal bearings which use oil as a lubrication fluid. As shown in FIG.1, the bearing system includes a journal 130 and a stationary part 120.The journal 130, functioning to transmit power, is supported by thejournal bearings 110. The journal bearings 110 are secured to thestationary part 120 which is made of a metal. Thus, heat generated inthe journal bearings 110 is transmitted through the journal bearings 110to the stationary part 120. When the temperature of lubricating oilrises in the journal bearings 110, thus the viscosity of the oil isreduced, and thereby a breakage of a lubrication film may be caused.Accordingly, in order to prevent the breakage of the oil film, heatconductivity of each journal bearing 110 is one of very importantcharacteristics of a bearing.

Further, when the journal 130 starts or stops rotating, there is noenough pressure generated to support the journal 130 by a lubricationoil film, so that boundary lubrication condition occurs, that is, a partof each journal bearing 110 is in direct contact with the journal 130.When the journal bearings 110 are broken or damaged due to the contactbetween the journal 130 and the journal bearings 110 under the boundarylubrication condition, the friction coefficient and relative hardnessbetween the journal 130 and the journal bearings 110 are recognized asimportant factors for bearing characteristics. When the journal 130 isdriven under the boundary lubrication condition, a surface of thejournal 130 may be damaged due to the contact between the journal 130and the journal bearings 110. Further, viscosity of the lubrication oilis reduced by heat generated due to the contact between the journal 130and each journal bearing 110, and a load bearing capacity of eachjournal bearing 110 is reduced, so that each journal bearing 110 may beundesirably adhered to the journal 130, thus causing seizure of eachjournal bearing 110 to the journal 130. Meanwhile, when an excessiveload acts on each journal bearing 110 or viscosity of the lubricationoil is reduced, the oil film becomes thin, so that the above problemsmay occur.

Thus, in order to protect the rotating journal 130 and reduce generationof heat due to the friction between the journal 130 and each journalbearing 110, each journal bearing 110 must be made of a material whichhas lower hardness compared to the journal 130, and a lower frictioncoefficient and a high thermal conductivity coefficient.

Now, a white metal has been widely used as a material of a liner of thejournal bearing. The liner is laminated to an inner surface of a metalhousing having a circular cross-section. The white metal is an alloyincluding tin, lead, antimony, and copper, and meets the above-mentionedrequirements of the journal bearing. However, the white metal hasproblems as follows. That is, since the white metal is a kind of metal,the white metal may be undesirably adhered to the journal made of ametal, due to melting caused when the white metal of the journal bearingis in direct contact with the journal and thereby temperature rises.Meanwhile, when the journal is made of a non-metal material, such as acomposite, the journal may be broken or damaged due to relatively higherhardness of the white metal when there is friction between the journalbearing and the journal.

The journal bearing may be integrally manufactured using a glass fiberreinforced phenol composite which has a lower friction coefficient andrelatively lower hardness. However, such a journal bearing is made ofonly the composite, so that the thickness of the journal bearing isincreased. Due to the increased thickness, a physical property isdeteriorated during the curing of the composite, and oil is absorbed inthe composite during the operation of the journal bearing, so thatdimensional precision is reduced, thus causing the journal bearing to beunstably driven. Thereby, the journal bearing may be broken or damaged.Further, since the composite absorbs oil during the operation of thejournal bearing, the lubrication film is destroyed during the operationof the journal bearing or the oil film becomes thin, so that the journalbearing may be severely damaged.

DISCLOSURE OF THE INVENTION

Accordingly, the present invention has been made keeping in mind theabove problems occurring in the prior art, and an object of the presentinvention is to provide a hybrid composite journal bearing which isconstructed so that a thin composite liner with low friction coefficientis positioned on the inner surface of a metal housing having a circularcross-section, thus minimizing damage to a journal due to frictionbetween the journal bearing and the journal.

Another object of the present invention is to provide a method ofmanufacturing the hybrid composite journal bearing, which is capable ofavoiding the seizure of the journal to the bearing.

In order to accomplish the above object, the present invention providesa hybrid composite journal bearing, including a metal housing which issecured to a stationary part of a bearing system and supports a journalof the bearing system so that the journal is rotatable, and a compositeliner which is laminated to an inner surface of the metal housing so asto minimize friction between the journal and the bearing and to increasethermal conductivity through bearing thickness.

Further, in order to accomplish the above object, the present inventionprovides a hybrid composite journal bearing, including a metal housingwhich is secured to a stationary part of a bearing system and supports ajournal of the bearing system so that the journal is rotatable, acomposite liner which is laminated to a predetermined portion of thejournal where the metal housing is placed, and arranged in the metalhousing, and a lubrication oil film which is provided between thecomposite liner and the metal housing.

In order to accomplish the above object, the present invention providesa method of manufacturing a hybrid composite journal bearing including ametal housing which is secured to a stationary part of a bearing systemand supports a journal of the bearing system so that the journal isrotatable, the method including winding a composite prepreg with variouslaminated angles around a mandrel, with a release agent being coated onan outer surface of the mandrel, inserting the mandrel around which thecomposite prepreg is wound into the metal housing, and then, removingthe mandrel from the metal housing, wrapping the composite prepreg andthe metal housing with a vacuum bag, forming a vacuum in the vacuum bagso that the composite prepreg is in close contact with an inner surfaceof the metal housing, and putting the metal housing with the compositeprepreg into an autoclave and curing the composite prepreg, and then,removing the vacuum bag.

In order to accomplish the above object, the present invention providesa method of manufacturing a hybrid composite journal bearing including ametal housing which is secured to a stationary part of a bearing systemand supports a journal of the bearing system so that the journal isrotatable, the method including winding a composite prepreg with variouslaminated angles around a mandrel which is thermally expansible,inserting the mandrel around which the composite prepreg is wound intothe metal housing, and putting the metal housing with the mandrel intoan autoclave to thermally expand the mandrel so that the compositeprepreg is cured while being in close contact with an inner surface ofthe metal housing, and removing the mandrel from the metal housing whichis taken out of the autoclave.

Further, in order to accomplish the above object, the present inventionprovides a method of manufacturing a hybrid composite journal bearingincluding a metal housing which is secured to a stationary part of abearing system and supports a journal of the bearing system so that thejournal is rotatable, the method including covering each of oppositeends of a reinforcing unit having a fiber preform and a film with acover, and placing the reinforcing unit into a metal housing, andsecuring the reinforcing unit in the metal housing by a support unit,feeding compressed air into the film so that the fiber preform is inclose contact with an inner surface of the metal housing, injecting aresin into the reinforcing unit so that the resin is impregnated intothe fiber preform, and supplying hot air into the film to harden thefiber preform impregnated with the resin, and removing the support unitand the cover from the metal housing, thus forming a composite liner.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, features and other advantages of thepresent invention will be more clearly understood from the followingdetailed description taken in conjunction with the accompanyingdrawings, in which:

FIG. 1 is a schematic view to show a bearing system equipped withconventional journal bearings;

FIG. 2 is a perspective view of a hybrid composite journal bearing,according to the first embodiment of the present invention;

FIG. 3 is a sectional view taken along the line A-A of FIG. 2;

FIG. 4 is a sectional view of a hybrid composite journal bearing,according to a modification of the first embodiment;

FIGS. 5 and 6 are views to show methods of manufacturing the hybridcomposite journal bearing of FIG. 2, through a simultaneous curingprocess;

FIG. 7 is a view to show a method of manufacturing the hybrid compositejournal bearing of FIG. 2, through an adhesive bonding process;

FIG. 8 is a view to show a method of manufacturing the hybrid compositejournal bearing of FIG. 2, through a resin transfer molding process;

FIG. 9 is an exploded perspective view of a hybrid composite journalbearing, according to the second embodiment of the present invention;and

FIG. 10 is a sectional view of the hybrid composite journal bearing ofFIG. 9.

BEST MODE FOR CARRYING OUT THE INVENTION

Reference should now be made to the drawings, in which the samereference numerals are used throughout the different drawings todesignate the same or similar components.

FIG. 2 is a perspective view of a hybrid composite journal bearing,according to the first embodiment of the present invention, FIG. 3 is asectional view taken along the line A-A of FIG. 2, and FIG. 4 is asectional view of a hybrid composite journal bearing, according to amodification of the first embodiment.

As shown in FIGS. 2 through 4, the hybrid composite journal bearing 210includes a metal housing 211 and a composite liner 212. The metalhousing 211 is secured on an outer surface thereof to a journal bearingsystem, and has a circular cross-section. The composite liner 212 islaminated to an inner surface of the metal housing 211 with a uniformthickness so as to minimize friction between the journal bearing 210 anda journal of the bearing system.

The metal housing 211 is secured to a stationary part 120 of the journalbearing system, in a same manner as the journal bearing 110 of FIG. 1.It is unnecessary for the outer surface of the metal housing 211 to havea circular shape of FIGS. 2 through 4. That is, the shape of the outersurface of the metal housing 211 does not matter, if only the metalhousing 211 is secured by the stationary part 120. However, an interiorof the metal housing 211 must have a circular cross-section, because thejournal having a circular cross-section is rotatable in the metalhousing 211. Therefore, a housing for a conventional journal bearing maybe used, in place of the metal housing 211 of this invention. Further,it is preferable that the metal housing 211 be made of a material havinga high thermal conductivity, such as cast iron, aluminum alloy, and ababbit metal, so that heat generated during the rotation of the journalis easily transmitted to the stationary part.

Further, in view of a characteristic of the composite, the compositeliner 212 has lower hardness than a conventional metallic journal buthas the same hardness as a composite journal. It is possible tomanufacture the composite liner 212, using various kinds of fibers andvarious kinds of resins. For example, the material of the compositeliner 212 may be selected out of carbon fiber reinforced phenolcomposite including carbon fiber and phenol resin, carbon fiberreinforced epoxy composite including carbon fiber and epoxy resin, glassfiber reinforced epoxy composite including glass fiber and epoxy resin,glass fiber reinforced polyester composite including glass fiber andpolyester resin, and others.

Of the above-mentioned composites, it is most preferable that thecomposite liner 212 be made of the carbon fiber reinforced phenolcomposite including carbon fiber and phenol resin. Since the carbonfiber reinforced phenol composite contains carbon fiber with anexcellent lubrication characteristic, the carbon fiber reinforced phenolcomposite reduces the damage of the journal when there is a directcontact between the journal and the composite liner 212. Further, thecarbon fiber has a higher thermal conductivity than the glass fiberwhich has been generally used, so that the carbon fiber efficientlytransmits heat generated during the rotation of the journal through themetal housing 211 to the stationary part of the bearing system, thusenhancing the heat conductivity of the journal bearing 210.

Preferably, the composite liner 212 is laminated to the inner surface ofthe metal housing 211 with a relatively thin thickness. That is, thecomposite liner 212 functions to prevent the seizure between the journaland the journal bearing 210. As the composite liner 212 is thinner, souse of the expensive carbon fiber reinforced composite is minimized,thus reducing costs of the carbon fiber reinforced composite. Further,the thin composite liner 212 prevents oil from being undesirablyabsorbed, which reduces the dimensional change.

As such, the journal bearing 210 is constructed so that the compositeliner 212 is provided on the inner surface of the metal housing 211 witha uniform thickness. However, according to the present invention, thecomposite liner 212 of the journal bearing 210 may be have tapered parts213 which are tapered from an interior to an exterior of the compositeliner 212. The formation of the tapered parts 213 on the composite liner212 is advantageous particularly when the journal bearing 210 is appliedto a large-sized journal, such as a journal for ships, which may sag bygravity. Due to the sag of the journal, a gap between the journal andthe journal bearing 210 is changed, and further, distribution ofpressure generated during the rotation of the journal is changed. Thus,when the amount of sag of the journal is large, the tapered parts 213are provided at the opposite ends of the composite liner 212 consideringthe sag of the journal, thus preventing the composite liner 212 frombeing in surface contact with the journal due to the sag of the journalduring the rotation of the journal.

Further, in the journal bearing 210 of this invention, it is preferablethat a white metal 214 with excellent deformability be laminated to eachend of the metal housing 211, as shown in FIG. 4, so that the oppositeends of the journal bearing 210 are deformed according to the amount ofsag of the large-sized journal which may sag due to gravity. That is,the composite liner 212 is laminated to a large part of the innersurface of the metal housing 211, and the white metals 214 arerespectively laminated at the outer ends of the metal housing 211 to beplaced at sides of the composite liner 212.

The method of manufacturing the hybrid composite journal bearingconstructed as described above will be described in the following indetail.

FIGS. 5 and 6 are views to show methods of manufacturing the hybridcomposite journal bearing of this invention, through a simultaneouscuring process. As shown in FIGS. 5 and 6, the hybrid composite journalbearing 210 is manufactured through the simultaneous curing process.

As shown in FIG. 5, a composite prepreg 222 having various laminatedangles, such as 0°, 90°, etc., is wound around a mandrel 224 to which arelease agent is coated. Subsequently, the mandrel 224 around which thecomposite prepreg 222 is wound is inserted into the metal housing 211.Next, the mandrel 224 is removed from the metal housing 211. Thereafter,the composite prepreg 222 and the metal housing 211 are wrapped with avacuum bag 223 so that the vacuum bag 223 is in close contact with aninner surface of the prepreg 222. Next, a vacuum is applied to theinside of the vacuum bag 223 so that the composite prepreg 222 is inclose contact with the inner surface of the metal housing 211. In such astatus, the metal housing 211 is put in an autoclave and cured for apredetermined period, and then the vacuum bag 223 is removed. In thisway, the composite liner 212 is laminated to the inner surface of themetal housing 211, thus the molding of hybrid composite journal bearingof this invention is completed.

Further, as shown in FIG. 6, the composite prepreg 222 having variouslaminated angles, such as 0°, 90°, etc., is wound around a mandrel 225made of a material having a high thermal expansive coefficient, such assilicon rubber. In this case, a release agent is coated on the mandrel225. Thereafter, the mandrel 225 around which the composite prepreg 222is wound is inserted into the metal housing 211. Next, the metal housing211 with the mandrel 225 is placed in an autoclave and cured for apredetermined period. At this time, the mandrel 225 thermally expands sothat the composite prepreg 222 is cured while being in close contactwith the inner surface of the metal housing 211. When the curing processis completed, the metal housing 211 with the mandrel 225 is taken out ofthe autoclave, and the mandrel 225 is removed from the metal housing211. In this way, the composite liner 212 is laminated to the innersurface of the metal housing 211, so that the molding of hybridcomposite journal bearing 210 of this invention is completed.

FIG. 7 is a view to show a method of manufacturing the hybrid compositejournal bearing of this invention, through an adhesive bonding process.As shown in FIG. 7, the hybrid composite journal bearing 210 may bemanufactured through the adhesive bonding process. That is, when it isdifficult to manufacture the hybrid composite journal bearing throughthe co-curing process, the cured composite liner 212 may be joined tothe inner surface of the metal housing 211 using an adhesive 226, asshown in FIG. 7, thus the hybrid composite journal bearing 210 ismanufactured. The adhesive 226 may be selected out of an epoxy agent, anepoxy agent containing an elastomer, a cyanoacrylate adhesive, apolyurethane adhesive, etc.

FIG. 8 is a view to show a method of manufacturing the hybrid compositejournal bearing of this invention, through a resin transfer moldingprocess. As shown in FIG. 8, the hybrid composite journal bearing 210may be manufactured through the resin transfer molding process. That is,the journal bearing of this invention includes a reinforcing unit,covers 243, and support units 245. The reinforcing unit includes a fiberpreform 241 and a soft film 242. An air inlet port 244 is provided at apredetermined portion of each of the covers 243. The support units 245support the reinforcing unit and the covers 243 to the metal housing211, with a resin inlet port 246 and an air outlet port 247 beingrespectively provided on each of the support units 245. The method ofmanufacturing the hybrid composite journal bearing through the resintransfer molding process is as follows.

First, both ends of the reinforcing unit having the fiber preform 241and the film 242 are sealed with the covers 243. At this time, an O-ring248 is fitted over an outer circumferential surface of each cover 243 soas to seal a gap between the film 242 and each cover 243. Thereafter,the reinforcing unit is positioned in the metal housing 211, and thenthe covers 243 are secured to the metal housing 211 using the supportunits 245.

Next, compressed air is fed into the film 242 through the air inlet port244 so that the film 242 is in close contact with the fiber preform 241,thus preventing the reinforcing unit from being wrinkled or twisted whenthe reinforcing unit is inserted into the metal housing 211. Further, bythe supply of the compressed air, the fiber preform 241 is in closecontact with the inner surface of the metal housing 211.

Next, after pressure in the film 242 is eliminated, resin is injected tothe fiber preform 241 through the resin inlet port 246 provided at apredetermined position of one of the support units 245, so that theresin is impregnated into the fiber preform 241. In this case, it ispreferable to use phenol resin as the matrix of composite. In order toreduce pressure required for the resin transfer, the resin may be heatedat about 60° so that viscosity thereof is reduced, prior to supplyingthe resin into the fiber preform 241. After injecting the resin into thefiber preform 241, hot air is supplied into the film 242 through acompressor equipped with a heater, thus pressurizing the film 242.Thereby, the reinforcing unit is in close contact with the inner surfaceof the metal housing 211, and further, air bubbles remaining in thefiber preform 241 are discharged to an outside through the air outletport 247, so that the resin is gradually cured. At this time, a vacuumpump is connected to the air outlet port 247 to form vacuum, thusallowing the resin to be smoothly impregnated into the fiber preform241, and efficiently removing air bubbles from the fiber preform 241,therefore maintaining a high fabric percentage by volume.

As such, the resin is cured after being impregnated into the fiberpreform 241, so that the composite liner 212 is formed in the metalhousing 211. At this time, the support units 245 and the covers 243 areremoved from the metal housing 211, so that the molding of hybridcomposite journal bearing 210 of this invention is completed. In thiscase, the film 242 may be removed as necessary.

The method of manufacturing the journal bearing through the resintransfer molding process can be applied to repairing or rehabilitatingof a journal bearing which is commonly used. For example, the compositeliner is formed in the metal housing through the resin transfer moldingprocess, without removing the metal housing of the journal bearing whichis secured to the stationary part, such as a ship, so that it ispossible to repair the journal bearing. Thus, the method ofmanufacturing the journal bearing through the resin transfer moldingprocess is suitable for insitu-repairing of a journal bearing for alarge vessel which is used for a lengthy period.

In the hybrid composite journal bearing 210 of this inventionmanufactured as described above, as shown in FIG. 1, the metal housing211 is secured to the stationary part 120, and the journal 130 isinserted into the composite liner 212. At this time, a lubrication oilfilm 111 is provided between the composite liner 212 and the journal130.

In the hybrid composite journal bearing 210 constructed as describedabove, the composite liner 212 is laminated to the inner surface of themetal housing 211, thus reducing the friction between the journalbearing 210 and a journal 233, and preventing the journal bearing 210from being seized to the journal 233.

FIG. 9 is an exploded perspective view of a hybrid composite journalbearing, according to the second embodiment of the present invention,and FIG. 10 is a sectional view of the hybrid composite journal bearingof FIG. 9.

As shown in FIGS. 9 and 10, when it is difficult to attach a compositeto the journal bearing, the composite prepreg is laminated to a positionof the journal 233 to which the journal bearing is mounted, and then iscured, so that the composite liner 232 is formed. Next, the compositeliner 232 is positioned in the metal housing 231, thus the molding ofhybrid composite journal bearing is completed. At this time, alubrication oil film 234 is provided between the composite liner 232 andthe metal housing 231.

When the hybrid composite journal bearing is manufactured as shown inFIGS. 9 and 10, a frictional coefficient between the journal bearing andthe journal 233 is reduced, and further, the seizure of the journalbearing and the journal is prevented.

INDUSTRIAL APPLICABILITY

As described above, the present invention provides a hybrid compositejournal bearing, which is constructed so that a thin composite liner isprovided on an inner surface of a metal housing having a circularcross-section, thus preventing a journal from being damaged or seized tothe bearing, due to friction between the metal or composite journal andthe journal bearing.

Further, the present invention provides a hybrid composite journalbearing, which used small amount of expensive composite, thusaccomplishing excellent performance per bearing material cost.

The present invention provides a hybrid composite journal bearing, whichcan be manufactured through a relatively simple method, such as theco-curing process, the adhesive bonding process, or the resin transfermolding process, as compared to conventional methods where a white metalis cast on a metal housing, or a thick glass fiber reinforced phenolcomposite is interferenced fitted, thus simplifying the manufacturingmethod and considerably reducing manufacturing costs thereof.

Further, the present invention provides a hybrid composite journalbearing, which is constructed to replace only the composite liner to bereplaced with a new one when the journal bearing is damaged, thus beingeasy to repair.

Although the preferred embodiments of the present invention have beendisclosed for illustrative purposes, those skilled in the art willappreciate that various modifications, additions and substitutions arepossible, without departing from the scope and spirit of the inventionas disclosed in the accompanying claims.

1.-8. (canceled)
 9. A method of manufacturing a hybrid composite journalbearing having a metal housing secured to a stationary part of a bearingsystem and supporting a journal of the bearing system in a manner thatthe journal is rotatable, the method comprising the steps of: winding acomposite prepreg with various laminated angles around a mandrel whichis thermally expansible; inserting the mandrel around which thecomposite prepreg is wound into the metal housing, and placing the metalhousing with the mandrel in an autoclave to thermally expand the mandrelso that the composite prepreg is cured while being in close contact withan inner surface of the metal housing; and removing the mandrel from themetal housing which is taken out of the autoclave. 10.-11. (canceled)